Amer Copper Acid Cleaning Fluid PGSX0001

Product brief introduction:

Amer Copper Acid Cleaning Fluid PGSX0001 is suitable for cleaning the oxidation layer, foreign matter, verdigris, 

polishing and bright dipping of brass, red brass, red copper, pure copper and copper alloy. It specially applies to further remove 

the pale brown and even black oxidation layer of brass after hot treatment. The color of treated surface is similar with the effect 

of traditional chromate treatment and the hardness of polished surface is moderate, particularly suitable for drawing treatment in subsequent. 

The product is the latest product replacing the current "three-acid" process and chromic acid cleaning process.

Performance advantages: 

1. Applicability: it's suitable for cleaning and bright dipping of all brass, red copper and the copper alloy and oxidation layer, particularly 

suitable for cleaning of serious oxidation layer of copper wire after hot treatment to greatly improve the surface glossiness. 

2. High efficiency: the process has the high speed of acid washing and polishing. Only 10s above, it can clean the oxidation layer and 

realize the bright dipping effect, and the glossiness is equivalent to the glossiness of chromate acid washing polishing agent and even brighter.

3. Stability: the product has the excellent stability and will not decompose and get invalid without the volatility. It has the long service life 

and is simple for maintenance. 

4. Environmental friendly: it does not contain the chromate and other toxic heavy metals as well as not contain the nitric acid and salts, 

conforming to the green and environmental requirements.

Main Application:

It's suitable for cleaning the oxidation layer, foreign matter, verdigris, polishing and bright dipping of brass, red brass, 

red copper, pure copper and copper alloy.

Instructions:

1. Proportion of adding water: 1:1~2 of adding water (it's recommended using the purified water) for diluting;

2. The 304 and 316 stainless steel or plastic container can be selected as the polishing tank; 

3. The plastic container is better to choose the PVC or PP material for making the tank and the size depends on the production capacity;

4. Treatment time: 10s-3min;

Application procedure:

1. Soak the copper parts in polishing fluid for 10s~3min (the time depends on severity of oxidation layer) and take it out, use the water 

to clean and the copper parts with the bright surface can be realized;

2. For making sure the polishing quality and service life of agent, it's better to conduct the acid cleaning in advance before acid cleaning and polishing;

3. When the serious oxidation layer on the surface of copper parts, it's recommended using 20~30% of  sulfuric acid to soak it for 1~3 min 

to clean the oxidation layer and then conducting acid cleaning and polishing;

4. Adding the process can greatly improve the acid cleaning speed and the agent service life, and then rinse it by using clean water. 

If not applicable, it needs replacing the tank liquid;

Precautions:

1. It cannot contact with steel part, carbon steel and other workpieces and will generate a large quantity of oxidation layer. 

The welding slags can be soaked in sulfuric acid and then treated by using polishing fluid;

2. After contacting with skin, use the clean water to rinse the skin; 

3. If it contacts with eyes, immediately use plenty of clean water to rinse the upper and lower eyelids and then go to the ophthalmology department for treatment; 

4. The storage tank and operation site conforms to all laws and regulations in current; 

5. It shall be stored in a cool, dry and well-ventilated place;

6. When not using it, please immediately seal the cover tightly and separate it from oxidizing agent and other incompatible substances for storage; 

Typical data: